Thermoluminescent Materials

In this paper, the thermoluminescence (TL) dosimetric characteristics under beta-ray, x-ray and gamma-ray excitations of powder and pellet Mn-doped lithium tetraborates (LTB) which were produced by solution combustion synthesis technique were investigated, and the results were compared with that of TLD-100 chips. The chemical composition and morphologies of the obtained LTB and Mn-doped LTB (LTB: Mn) were confirmed by X-ray diffraction (XRD), Fourier Transform Infrared (FTIR) and scanning electron microscopy (SEM) with EDX. LTB:Mn was studied using luminescence spectroscopy. In addition, the effects of sintering and annealing temperatures and times on the thermoluminescence (TL) properties of LTB:Mn were investigated. The glow curves of powder samples as well as pellet samples exposed to different beta doses exhibited a low temperature peak at about 100 °C followed by an intense principal high temperature peak at about 260 °C. The kinetic parameters (E, b, s) associated with the prominent glow peaks were estimated using T m –T stop , initial rise (IR) and computerized glow curve deconvolution (CGCD) methods. The TL response of integral TL output increased linearly with increasing the dose in the range of 0.1–10 Gy and was followed by a superlinearity up to 100 Gy both for powder and pellet samples using beta-rays. Powder and pellet LTB:Mn were irradiated to a known dose by a linear accelerator with 6 and 18 MV photon beams, 6–15 MeV electron beams and a traceable 137 Cs beam to investigate energy response. Further, TL sensitivity, fading properties and recycling effects related with beta exposure of LTB:Mn phosphor were evaluated and its relative energy response was also compared with that of TLD-100 chips. The comparison of the results showed that the obtained phosphors have good TL dose response with adequate sensitivity and linearity for the measurement of medical doses.

Factors affecting the random and systematic error in calibrating three sets of 100 LiF:Mg,Ti thermoluminescent detector chips were investigated. The chips were held in a polymethyl methacrylate plate with 0.3 cm deep wells covered with a thin top plate, affixed to a polymethyl methacrylate phantom 150 cm from a 3.2 × 1010 GBq 137Cs source, used to irradiate the chips to 4.52 mGy. Three sets of chips were used: one new, one heavily used, and one having relatively high degrees of visible physical damage. Variations in the exposure rate across the plate were measured with an ion chamber. Experimental drift was judged by performing successive calibrations on subsequent days, while always reading the chips in the same order. The chips were subject to manual examination to determine variations in mass and physical quality. This study indicates that more accurate calibrations can be obtained by accounting for the error caused by nonuniformity in the delivered dose, which was in this study as high as 4.4% from the center to the edges of the target. Making use of more than three calibrations only reduces the standard deviation as a percentage of the mean of a set by less than 1%. Desirable dosimeters in commercially rejected sets were identified by comparing each dosimeter's standard deviation of response across all calibrations to a commercially acceptable control set. Up to 50% variations in mass and visual quality, including opacity, fracture, and surface scratches to chips, showed little to no correlation with their response.